Cordierite Mullite Kiln Furniture Perforated Extruded Batts for Sanitaryware

Cordierite Mullite Kiln Furniture Perforated Extruded Batts for Sanitaryware

Cordierite is commonly used to make kiln furniture for refractory applications, due to its good thermal shock properties, low thermal expansion and thermal conductivity. it is a group of cost-effective material, widely used to hold and support products during heat-treatment processes (such as firing or sintering) at temperatures up to 1300 ºC

Quantity:
Max.Working Temperature:	1300 ºC
Density :	1850-2050 KG/M3
APPLICATIONS:	TABLEWARE , SANITARY WARE ETC
SHAPE AVAILABLE :	kiln shelves, batts, cover batts, tubes and beams, props and fittings, profile setters, saggars, stools, T-cranks, Y-cranks and pin-crank systems.
Material:	Cordierite
Availability:




Inquire Add to Basket

Model: YUFNEGREC-KFA, KFB, KFC
Brand: YUFENGREC
Code: 69022000

Product Description

YUFENGKF-Cordierite-Mullite is a combination of Cordierite Phase ,Mullite Phase and Glass Phase , feature with excellent thermal shock resistance ,high temperature resistance ,which is the most suitable material making kiln furniture especially service under 1300 Deg C .

Cordierite-Mullite Kiln Furniture are widely used in the Table Ware , Sanitary ware , Electrical Porcelain Insulator , Powder Calcination , Technical Ceramic industry .

Cordierite Mullite Kiln Furniture Shapes

Kiln Shelves / Batts / Cranks
Setters / Supports / Cranks
Ceramic Tubes / Fitting / Props
Saggar / Crucibles
Kiln Car Structures
Pizza Plates

Features of Cordierite Mullite Kiln Furniture

Extremely Thermal Shock Resistant
Stable under high temperature
Low density
Excellent dimensional accuracy control

Technical Data Sheet

Item	Unit	BRAND
Item	Unit	YUFENG-KFA	YUFENG-KFB	YUFENG-KFC
AI₂O₃	%	35	39	60
SiO₂	%	53	49	35
MgO	%	7.5	8.0	5.0
Max Working Temperature	ºC	1280	1260	1350
Bulk Density	g/cm³	1.85	1.82	2.20
Apparent Porosity	%	28	30	22
Coefficient of Thermal Expansion at 20ºC - 1000ºC	10^-6k^-1	2.6	2.2	3.2
Specific Heat at 20ºC	Kj/Kg.k	1.0	1.0	1.0
M.O.R. at 20ºC	MPa	14	11	11
M.O.R. at 1250ºC	MPa	10	10	10
Thermal Shock Resistance		Excellent	Excellent	Excellent
Max Working Temperature	ºC	1280	1280	1350