IFB2300
YUFENGREC
69022000
Insulating Fire Brick JM23 With Light Weight For Furnace Insualtion
YUFENGREC®Insulating Fire Brick are made of high-grade refractory powder and material in good purity . During the process of production , organic and multiple filling materials are injected according to there required proportion ,the brick is compressed in vacuum and sintered under high temperature , for use in applications from 2300ºF (1260ºC) to 3000ºF (1650ºC).
Each type is formulated to meet specific thermal and physical requirements, and after firing is machined to precise tolerances. Made from high purity refractory clays and other ceramic raw materials, these IFB contain carefully graded organic filler which is burned out during manufacture to give a uniform, controlled pore structure.
Key Features
* Low iron content
* Resistance to thermal shock
* Low density
* Low heat storage
* High insulating properties
* Energy saving
Typical Applications
* Primary hot face linings
* Back-up insulation for furnaces and kilns
* Flue insulation
* Sulphur recovery equipment .
* Hot blast soves
* Cracking Furnace
* Ceramic Industry
* Continuous and batch kilns
* Power Generation
* Boiler insulation etc …
Technical Data Sheet
| ITEM | YUFENGREC-IFB2300 | |
| Classification Temp. ASTM C155-97 | 1260 ºC | |
| Bulk Density ASTM C134-95 | 600 kg/m3 | |
| Cold Crushing Strength ASTM C133-97 | 1.2 MPa | |
| Modulus of Rupture ASTM C133-97 | 1.0 MPa | |
| Permanent Linear Change ASTM C210-95 | % | -0.2 |
| ºCxh | 1230 x 24 | |
Thermal Conductivity ASTM C182-88 | 400ºC | 0.17 |
| 600ºC | 0.19 | |
| 800ºC | 0.22 | |
| 1000ºC | 0.25 | |
| Chemical Analysis | ||
| Al2O3 | 45% | |
| Fe2O3 | 0.9% | |
| SiO2 | 51% | |
| K2O+Na2O | 1.5% | |
*The data are average results of test under standard procedures and are subject to variation. Results should not be used for specification purposes or creating any contractual obligation.
QC Inspections
Packing and Loading
Applications
Insulating Fire Brick JM23 With Light Weight For Furnace Insualtion
YUFENGREC®Insulating Fire Brick are made of high-grade refractory powder and material in good purity . During the process of production , organic and multiple filling materials are injected according to there required proportion ,the brick is compressed in vacuum and sintered under high temperature , for use in applications from 2300ºF (1260ºC) to 3000ºF (1650ºC).
Each type is formulated to meet specific thermal and physical requirements, and after firing is machined to precise tolerances. Made from high purity refractory clays and other ceramic raw materials, these IFB contain carefully graded organic filler which is burned out during manufacture to give a uniform, controlled pore structure.
Key Features
* Low iron content
* Resistance to thermal shock
* Low density
* Low heat storage
* High insulating properties
* Energy saving
Typical Applications
* Primary hot face linings
* Back-up insulation for furnaces and kilns
* Flue insulation
* Sulphur recovery equipment .
* Hot blast soves
* Cracking Furnace
* Ceramic Industry
* Continuous and batch kilns
* Power Generation
* Boiler insulation etc …
Technical Data Sheet
| ITEM | YUFENGREC-IFB2300 | |
| Classification Temp. ASTM C155-97 | 1260 ºC | |
| Bulk Density ASTM C134-95 | 600 kg/m3 | |
| Cold Crushing Strength ASTM C133-97 | 1.2 MPa | |
| Modulus of Rupture ASTM C133-97 | 1.0 MPa | |
| Permanent Linear Change ASTM C210-95 | % | -0.2 |
| ºCxh | 1230 x 24 | |
Thermal Conductivity ASTM C182-88 | 400ºC | 0.17 |
| 600ºC | 0.19 | |
| 800ºC | 0.22 | |
| 1000ºC | 0.25 | |
| Chemical Analysis | ||
| Al2O3 | 45% | |
| Fe2O3 | 0.9% | |
| SiO2 | 51% | |
| K2O+Na2O | 1.5% | |
*The data are average results of test under standard procedures and are subject to variation. Results should not be used for specification purposes or creating any contractual obligation.