YUFENGREC ® LP-12, YUFENGREC ® LP-14, YUFENGREC ® LP-17,
YUFENGREC®
69022000
YUFENGREC® Special High Quality Refractory Fire clay Brick are made of pure and high grade raw material producing by drying pressing and high fired ,with lower porosity ,high crushing strength .
Classification : ASTM C-27
Method of Manufacturer: Dry Pressing
Key Features
* High Strength
*Lower Shrinkage
*Low Apparent Porosity
*Excellent Alkalis Resistant
*Good resistant to Thermal Shock
*High Refractoriness under load
*Good Creep Rate under high temp.
Typical Applications
* Glass Furnace
* Blast Furnace
* Hot Blast Stove
* Cement Rotary Kiln
* Kinds of high temperature industry furnace
Dimensions
*230 x 114 x 64 mm
*230 x 114 x 76 mm
*Customized production for bricks with special dimension is available
Packing
In export standard wooden pallet
More detail techinal data and MSDS information, please contact us: tom@yufengrefractory.com
Technical Data
| Item | Unit | Low Apparent Porosity Fire Brick | ||
| YUFENGREC® LP12 | YUFENGREC® LP14 | YUFENGREC® LP17 | ||
| Al2O3 | % | ≥46 | ≥45 | ≥42 |
Fe2O3 | % | ≤1.20 | ≤1.50 | ≤1.80 |
| Bulk Density | g/cm3 | ≥2.40 | ≥2.34 | ≥2.29 |
| Apparent Porosity | % | ≤12 | ≤14 | ≤17 |
| Cold Crushing Strength | MPa | ≥80 | ≥65 | ≥5 |
| Permanent Linear Change at 1400℃ x2h | % | - - - - - | +0.1 to -0.2 | +0.1 to -0.2 |
| Refractoriness Under Load 0.2 MPa | ℃ | 1520 | 1470 | 1430 |
| Creep Rate 0.2 MPa under 1200℃ x 50 h | % | 0.1 | - - - - - | - - - - - |
The data are average results of tests under standard procedures and are subject to variation. Results should not be used for specification purposes or creating any contractual obligation. For more information on the safety applications or materials ,please refer to the work practices and material safety data sheet
YUFENGREC® Special High Quality Refractory Fire clay Brick are made of pure and high grade raw material producing by drying pressing and high fired ,with lower porosity ,high crushing strength .
Classification : ASTM C-27
Method of Manufacturer: Dry Pressing
Key Features
* High Strength
*Lower Shrinkage
*Low Apparent Porosity
*Excellent Alkalis Resistant
*Good resistant to Thermal Shock
*High Refractoriness under load
*Good Creep Rate under high temp.
Typical Applications
* Glass Furnace
* Blast Furnace
* Hot Blast Stove
* Cement Rotary Kiln
* Kinds of high temperature industry furnace
Dimensions
*230 x 114 x 64 mm
*230 x 114 x 76 mm
*Customized production for bricks with special dimension is available
Packing
In export standard wooden pallet
More detail techinal data and MSDS information, please contact us: tom@yufengrefractory.com
Technical Data
| Item | Unit | Low Apparent Porosity Fire Brick | ||
| YUFENGREC® LP12 | YUFENGREC® LP14 | YUFENGREC® LP17 | ||
| Al2O3 | % | ≥46 | ≥45 | ≥42 |
Fe2O3 | % | ≤1.20 | ≤1.50 | ≤1.80 |
| Bulk Density | g/cm3 | ≥2.40 | ≥2.34 | ≥2.29 |
| Apparent Porosity | % | ≤12 | ≤14 | ≤17 |
| Cold Crushing Strength | MPa | ≥80 | ≥65 | ≥5 |
| Permanent Linear Change at 1400℃ x2h | % | - - - - - | +0.1 to -0.2 | +0.1 to -0.2 |
| Refractoriness Under Load 0.2 MPa | ℃ | 1520 | 1470 | 1430 |
| Creep Rate 0.2 MPa under 1200℃ x 50 h | % | 0.1 | - - - - - | - - - - - |
The data are average results of tests under standard procedures and are subject to variation. Results should not be used for specification purposes or creating any contractual obligation. For more information on the safety applications or materials ,please refer to the work practices and material safety data sheet