YUFENGREC® Cordierite-Mullite Kiln Furniture -Plain Batts manufactured by synthetic cordierite and lower alumina mullite ,through unique scientific formula proportion of fines and aggregate , formed by vacuum extruding process , fired under high temperature . It has excellent thermal shock resistance, low creep rate , stable at high temperature performance . it is the best kiln furniture material operating between 1000-1300ºC，
Plain Batts is considering and designing about the materials, proportionning and performance index .Iti s one of the popluar kiln furniture .Most of the batts are made by pressing , some of the thicker batts also can be extruding process . it was used to table ware , fooamed ceramics ,building ceramics ,electric ceramics industry , our batts can basically meet all industries requirement .
Technical Data
Item | Unit | Typical Index |
Chemical Compositions | ||
AI2O3 | % | 45 |
SiO2 | % | 45 |
Fe2O3 | % | 0.65 |
MgO | % | 6.5 |
Physical Properties | ||
Bulk Density | g/cm3 | 2.05 |
Apparent Porosity | % | 23 |
Refractoriness Under Load | ℃ | 1420 |
Coefficient of Linear Thermal Expansion at 25℃ - 1000℃ | 10-6 .℃-1 | 2.4 |
M.O.R. at 20℃ | MPa | 12 |
M.O.R. at 1250℃ | MPa | 10 |
Thermal Shock Resistance 1100℃ water cooling | Circle | 40 |
Max Working Temperature | ℃ | 1250 |
The data are average results of test under standard procedures and are subject to variation. Results should not be used for specification purposes or creating any contractual obligation.
YUFENGREC® Cordierite-Mullite Kiln Furniture -Plain Batts manufactured by synthetic cordierite and lower alumina mullite ,through unique scientific formula proportion of fines and aggregate , formed by vacuum extruding process , fired under high temperature . It has excellent thermal shock resistance, low creep rate , stable at high temperature performance . it is the best kiln furniture material operating between 1000-1300ºC，
Plain Batts is considering and designing about the materials, proportionning and performance index .Iti s one of the popluar kiln furniture .Most of the batts are made by pressing , some of the thicker batts also can be extruding process . it was used to table ware , fooamed ceramics ,building ceramics ,electric ceramics industry , our batts can basically meet all industries requirement .
Technical Data
Item | Unit | Typical Index |
Chemical Compositions | ||
AI2O3 | % | 45 |
SiO2 | % | 45 |
Fe2O3 | % | 0.65 |
MgO | % | 6.5 |
Physical Properties | ||
Bulk Density | g/cm3 | 2.05 |
Apparent Porosity | % | 23 |
Refractoriness Under Load | ℃ | 1420 |
Coefficient of Linear Thermal Expansion at 25℃ - 1000℃ | 10-6 .℃-1 | 2.4 |
M.O.R. at 20℃ | MPa | 12 |
M.O.R. at 1250℃ | MPa | 10 |
Thermal Shock Resistance 1100℃ water cooling | Circle | 40 |
Max Working Temperature | ℃ | 1250 |
The data are average results of test under standard procedures and are subject to variation. Results should not be used for specification purposes or creating any contractual obligation.